Virgin HDPE White Plastic Particles for Woven Bags

• Customization: Available
• Carrier: HDPE
• Color: White
• Model NO.: 25213-02-9
• Certification: ISO
• Transport Package: Requirement
• Specification: Requirement
• Trademark: Kailiya
• Origin: China
• Production Capacity: 5000ton/Week

Product Description

Product Description

1.HDPE
High density Polyethylene (HDPE): is a highly crystalline non-polar thermoplastic resin produced through the copolymerization of ethylene and a small amount of α-olefin monomer. HDPE is synthesized under low pressure and is therefore also called low-pressure polyethylene. HDPE is mainly a linear molecular structure and has little branching. It has a high degree of crystallization and high density. It can withstand high temperatures and has good rigidity and mechanical strength and anti-chemical corrosion.
Properties:
High density polyethylene for non-toxic, tasteless, no smelly white particles, melting point is about 130 ° C, relative density of
0.941 ~ 0.960. It has good heat resistance and cold resistance, chemical stability, but also has high rigidity and toughness, good
mechanical strength. Dielectric properties, environmental stress cracking resistance sex also is good.

2.Specification:

 

Film Grade

Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C

Blown Grade

Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%

Injection grade

Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

3.Application:

1.Film grade is widely used in the production of packing bag, film and so on.
2.Blow molding grade for making various bottles, cans, tanks , barrels Injection-molding grade is for making food cases, plastic
trays, goods containers.
3.Blow film product:Foodstuff packing bag,groceries shopping bags, chemical fertilizer
lined with film, etc
4.Extruded product: Pipe,tube mainly used in gas transportation, public water and chemicals
transport, such as building materials, gas pipe, hot water drain pipe etc: sheet material is
mainly used in the seat, suitcase, handling containers.

4.Package&Storage&Transportation:

1.Packing:
25kg/ carton or 25kg/bag, or per your requirement.
18mt/20'FCL
2.Storage:
The resin should be stored in a drafty, dry warehouse and away from fire and direct sunlight. It should not be piled up in the open air.
3.Transportation:
During transportation, the product should not be exposed to strong sunlight or rain and should not be transported together with sand, soil, scrap metal, coal or glass. Transportation together with toxic, corrosive and flammable substance is strictly prohibited.

 

During transportation, the product should not be exposed to strong sunlight or rain and should not be transported together with sand, soil, scrap metal, coal or glass. Transportation together with toxic, corrosive and flammable substance is strictly prohibited.

 

 

 

Material	100% Virgin EVA resin
certificate	ISO
Application	for hot-melt
Appearance	Transparent Granule
Raw material	Ethylene-Vinyl  Acetate Copolymer
MOQ	25 kg
Certificates	COA MSDS TDS
Feature	excellent adhesion, high-flowability and soft properties
Usage	For Hot-melt
VA content	28%
Place of Origin	China
Brand Name	HJ
Model Number	For hot-melt

 

Detailed Photos

 

Packaging & Shipping

Company Profile